This study reports the effect of vanadium on the crystal structure and electrical and electrochemical properties of La0.6−x VxSr0.4MnO3−δ (x = 0.005–0.1) perovskite-based cathode materials in solid oxide fuel cells. Crystal structure, morphology, and porosity of prepared cathode materials are characterized by X-ray diffraction, X-ray photoelectron spectroscopy (XPS), and scanning electron microscopy. Using XPS analysis it was established that the La3+ cation is exchanged by the V4+/5+ cation in the perovskite structure. This ion replacement improves the ionic conductivity and catalytic activity for oxygen reduction reaction in the perovskite structure, presumably due to the smaller size of the V4+/5+ cation than the La3+ ion.
Nội dung trích xuất từ tài liệu:
Fabrication and electrochemical performance of La0.595V0.005Sr0.4MnO3−δ (LV05SM) cathode material for solid oxide fuel cells
Fabrication and electrochemical performance of La0.595V0.005Sr0.4MnO3−δ (LV05SM) cathode material for solid oxide fuel cells
Số trang: 31
Loại file: pdf
Dung lượng: 4.90 MB
Lượt xem: 10
Lượt tải: 0
Thông tin tài liệu:
Tìm kiếm theo từ khóa liên quan:
Journal of Chemistry Solid oxide fuel cells Oxygen reduction reaction Symmetric cells Electrochemical impedance spectroscopyTài liệu có liên quan:
-
13 trang 30 0 0
-
9 trang 29 0 0
-
14 trang 24 0 0
-
Removal of Cr(VI) from wastewater through glycine assisted synthesis of TiO2
9 trang 24 0 0 -
Influence of magnetic field on properties of electrodeposited FeCo layer
5 trang 23 0 0 -
10 trang 22 0 0
-
The role of diazacrown ether in the enhancement of the biological activity of silver nanoparticles
11 trang 21 0 0 -
16 trang 20 0 0
-
Spectroscopic investigation of defect-state emission in CdSe quantum dots
8 trang 20 0 0 -
17 trang 19 0 0